ASTM A514 Grade S is a high-strength, quenched and tempered alloy steel with the following properties:
| Property | Value |
|---|---|
| Yield Strength (min) | 690 MPa (100 ksi) |
| Tensile Strength | 760-895 MPa (110-130 ksi) |
| Elongation in 2″ (min) | 16-18% |
| Carbon Content | 0.11-0.21% |
| Manganese Content | 1.1-1.5% |
| Silicon Content | 0.15-0.45% |
ASTM A514 Grade S steel is commonly used in:
ASTM A514 Grade S is produced through quenching and tempering processes. Available dimensions include:
| Thickness (in/mm) | Width (in/mm) | Length (in/mm) |
|---|---|---|
| 0.188 – 2.00 | 72 – 120 | 240 – 600 |
| 4.78 – 50.8 | 1800 – 3050 | 6100 – 15200 |
ASTM A514 Grade S has good weldability but requires careful attention to welding procedures. Proper preheat and interpass temperatures should be maintained to prevent cracking.
Grade S offers similar yield and tensile strengths to other A514 grades, but has a slightly different chemical composition, particularly in manganese content.
While ASTM A514 Grade S has a higher initial cost, its high strength allows for thinner sections and reduced overall weight in structures, potentially leading to cost savings in material usage, transportation, and installation.
At HL Steel Company, we offer high-quality ASTM A514 Grade S steel coils tailored for various heavy equipment and structural applications, ensuring optimal performance and durability for your projects.
121, Building 114, Jiangsu Street, Wuzhou International Industrial Expo City, Xinwu District, Wuxi City,Jiangsu Province,China
Building 114, Jiangsu Street, Wuzhou International Industrial Expo City, Xinwu District, Wuxi City
We will contact you within 1 working day, please pay attention to the email with the suffix “[email protected]”.