Chemical Composition:
| Element | Percentage |
|---|---|
| C | 0.11% Max |
| Si | 0.30-0.50% |
| Mn | 1.10-1.35% |
| P | 0.02% Max |
| S | 0.006% Max |
| Ni | 0.25-0.40% |
| Cr | 0.45-0.70% |
| Cu | 0.25-0.40% |
| V | 0.04-0.08% |
| Mo | 0.02-0.08% |
Mechanical Properties:
| Property | Value |
|---|---|
| Yield Strength (min) | 345 MPa (50 ksi) |
| Tensile Strength (min) | 485 MPa (70 ksi) |
| Elongation in 200mm (min) | 18% |
| Elongation in 50mm (min) | 21% |
ASTM A709 Grade HPS 50W steel is primarily used in:
Advantages include:
HPS 50W is produced using conventional hot-rolling or controlled rolling processes. Available dimensions:
| Thickness | Width | Length |
|---|---|---|
| Up to 4 inches (100 mm) | 72 to 120 inches (1830 to 3050 mm) | Up to 1200 inches (30480 mm) |
| Grade | Yield Strength (min) | Tensile Strength (min) | Corrosion Resistance |
|---|---|---|---|
| 50 | 345 MPa (50 ksi) | 450 MPa (65 ksi) | Standard |
| 50W | 345 MPa (50 ksi) | 485 MPa (70 ksi) | Improved |
| HPS 50W | 345 MPa (50 ksi) | 485 MPa (70 ksi) | Enhanced |
| HPS 70W | 485 MPa (70 ksi) | 585 MPa (85 ksi) | High Performance |
HPS 50W offers enhanced atmospheric corrosion resistance with an ASTM G101 Atmospheric Corrosion Resistance Index of ≥6.0. This makes it suitable for use in exposed structures without painting in many environments.
HPS 50W can be welded with greater ease than many steels developed in the past. It follows standard welding procedures and does not typically require preheating or post-weld heat treatment for most applications.At HL Steel Company, we offer high-quality ASTM A709 Grade HPS 50W steel coils tailored for bridge construction and other structural applications, ensuring optimal performance and durability for your projects.
121, Building 114, Jiangsu Street, Wuzhou International Industrial Expo City, Xinwu District, Wuxi City,Jiangsu Province,China
Building 114, Jiangsu Street, Wuzhou International Industrial Expo City, Xinwu District, Wuxi City
We will contact you within 1 working day, please pay attention to the email with the suffix “[email protected]”.