A106 Grade A pipes have specific chemical and mechanical properties:Chemical Composition:
| Element | Maximum Percentage |
|---|---|
| Carbon | 0.25% |
| Manganese | 0.27-0.93% |
| Phosphorus | 0.035% |
| Sulfur | 0.035% |
| Silicon | 0.10% min |
Mechanical Properties:
| Property | Value |
|---|---|
| Tensile Strength (min) | 48,000 psi (330 MPa) |
| Yield Strength (min) | 30,000 psi (205 MPa) |
| Elongation (min) | 35% |
A106 Grade A pipes are used in various industries:
A106 Grade A pipes are manufactured as seamless pipes through hot rolling or cold drawing processes. They are available in:
| Property | A106 Grade A | A106 Grade B | A106 Grade C |
|---|---|---|---|
| Tensile Strength (min) | 48,000 psi | 60,000 psi | 70,000 psi |
| Yield Strength (min) | 30,000 psi | 35,000 psi | 40,000 psi |
| Carbon Content (max) | 0.25% | 0.30% | 0.35% |
A106 Grade A is suitable for low-pressure applications and does not require heat treatment after the final cold drawing process.
A106 Grade A pipes adhere to ASTM A106 / ASME SA106 standards and undergo various tests:
At HL Steel Company, we ensure that all our A106 Grade A pipelines meet or exceed these quality standards, providing our customers with reliable and high-performance products for their diverse industrial needs.